Creep-resistant, cobalt-containing alloys for high temperature, liquid-salt heat exchanger systems
Patent
·
OSTI ID:1462963
An essentially Fe-free alloy consists essentially of, in terms of weight percent: 4 to 11 Co, 6.5 to 7.5 Cr, 0 to 0.15 Al, 0.5 to 0.85 Mn, 11 to 20 Mo, 1 to 3.5 Ta, 0.05 to 9 W, 0.03 to 0.08 C, 0 to 0.001 B, 0.0005 to 0.005 N, balance Ni, the alloy being characterized by, at 850.degree. C., a yield strength of at least 25 Ksi, a tensile strength of at least 45 Ksi, a creep rupture life at 12 Ksi of at least 10 hours, and a corrosion rate, expressed in weight loss [g/(cm.sup.2sec)]10.sup.-11 during a 1000 hour immersion in liquid FLiNaK at 850.degree. C., in the range of 5 to 20.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-00OR22725
- Assignee:
- UT-Battelle, LLC (Oak Ridge, TN)
- Patent Number(s):
- 10,017,842
- Application Number:
- 13/958,672
- OSTI ID:
- 1462963
- Resource Relation:
- Patent File Date: 2013 Aug 05
- Country of Publication:
- United States
- Language:
- English
Similar Records
Creep-resistant, cobalt-free alloys for high temperature, liquid-salt heat exchanger systems
High strength alloys for high temperature service in liquid-salt cooled energy systems
Intermediate strength alloys for high temperature service in liquid-salt cooled energy systems
Patent
·
Tue Sep 06 00:00:00 EDT 2016
·
OSTI ID:1462963
High strength alloys for high temperature service in liquid-salt cooled energy systems
Patent
·
Tue Jan 10 00:00:00 EST 2017
·
OSTI ID:1462963
Intermediate strength alloys for high temperature service in liquid-salt cooled energy systems
Patent
·
Tue Jun 20 00:00:00 EDT 2017
·
OSTI ID:1462963